| Quantity: | |
|---|---|
LJ
Product Description:
| Blanks Tolerance | +/-0.3~+/-2 mm |
| Forging Blank Size /Dimensions | 142 mm- 300mm or according to customer requirement |
| Blanks Weight | Max10000kg |
| Production Process for Forged parts | Forging, press, plus machining ,heat treatment , assembly |
| Applicable Machining Process | CNC Machining/ Lathing/ Milling/ Turning/ Boring/ Drilling/ Tapping/ Broaching/Reaming etc. |
| Carried Out Detection | Chemical Composition,Mechanical Properties,Non Destructive Testing,Size,Hardness. |
| Applicable Heat Treatment | Normalization , quenching and tempering, Case Hardening, Nitriding, Carbon Nitriding, Induction Quenching. |
Stainless steel 1Cr18Ni9Ti is an ordinary stainless steel (SUS321), and its tissue category is Aobi body. 1Cr18Ni9Ti 1, 18, and 9 represent the content of carbon (‰), chromium (%), and nickel (%), respectively. It is used to make acid-resistant containers and equipment lining, anti-magnetic instrument and medical equipment, which has better corrosiveness of crystal resistance.
Chemical Composition (%)
| C | Si | Mn | S | P | Cr | Ni | Ti |
| ≤0.12 | ≤1.00 | ≤2.00 | ≤0.030 | ≤0.035 | 17.00～19.00 | 8.00～11.00 | 5(C%-0.02)～0.80 |
Mechanical Property
| Tensile Strength σb(MN/m2) | Yield Strength σs(MN/m2) | Elongation δ5（%） |
| ≥550 | ≥200 | ≥40 |
Product Description:
| Blanks Tolerance | +/-0.3~+/-2 mm |
| Forging Blank Size /Dimensions | 142 mm- 300mm or according to customer requirement |
| Blanks Weight | Max10000kg |
| Production Process for Forged parts | Forging, press, plus machining ,heat treatment , assembly |
| Applicable Machining Process | CNC Machining/ Lathing/ Milling/ Turning/ Boring/ Drilling/ Tapping/ Broaching/Reaming etc. |
| Carried Out Detection | Chemical Composition,Mechanical Properties,Non Destructive Testing,Size,Hardness. |
| Applicable Heat Treatment | Normalization , quenching and tempering, Case Hardening, Nitriding, Carbon Nitriding, Induction Quenching. |
Stainless steel 1Cr18Ni9Ti is an ordinary stainless steel (SUS321), and its tissue category is Aobi body. 1Cr18Ni9Ti 1, 18, and 9 represent the content of carbon (‰), chromium (%), and nickel (%), respectively. It is used to make acid-resistant containers and equipment lining, anti-magnetic instrument and medical equipment, which has better corrosiveness of crystal resistance.
Chemical Composition (%)
| C | Si | Mn | S | P | Cr | Ni | Ti |
| ≤0.12 | ≤1.00 | ≤2.00 | ≤0.030 | ≤0.035 | 17.00～19.00 | 8.00～11.00 | 5(C%-0.02)～0.80 |
Mechanical Property
| Tensile Strength σb(MN/m2) | Yield Strength σs(MN/m2) | Elongation δ5（%） |
| ≥550 | ≥200 | ≥40 |