GH4133B is the Ni-CR-CO base sedimentation and hardening high-temperature alloy, with a temperature below 750 degrees Celsius. The alloy has high yield intensity, good comprehensive mechanical performance, good antioxidant performance, uniform and small tissue-stable crystal grains, and easy to heat up.
Chemical Composition
C | Si | Mn | P | S | Cr | Ni | Mg | Co |
≤0.06 | ≤0.65 | ≤0.35 | ≤0.015 | ≤0.007 | 19-22 | Bal | 0.001-0.01 | 18-22 |
Cu | Fe | Nb | B | Ti | Al | V | Zr | Ce |
≤0.07 | ≤1.5 | 1.3-1.7 | ≤0.01 | 2.5-3 | 0.75-1.15 | - | 0.01-0.1 | ≤0.01 |
GH4133B is the Ni-CR-CO base sedimentation and hardening high-temperature alloy, with a temperature below 750 degrees Celsius. The alloy has high yield intensity, good comprehensive mechanical performance, good antioxidant performance, uniform and small tissue-stable crystal grains, and easy to heat up.
Chemical Composition
C | Si | Mn | P | S | Cr | Ni | Mg | Co |
≤0.06 | ≤0.65 | ≤0.35 | ≤0.015 | ≤0.007 | 19-22 | Bal | 0.001-0.01 | 18-22 |
Cu | Fe | Nb | B | Ti | Al | V | Zr | Ce |
≤0.07 | ≤1.5 | 1.3-1.7 | ≤0.01 | 2.5-3 | 0.75-1.15 | - | 0.01-0.1 | ≤0.01 |